This table contains mechanical property reference data for Stainless Steel.
This table includes Yield strength, Tensile strength, Elongation, Reduction in Area and Brinnel hardness information.
(Tabulated in accordance with the Unified Numbering System for Metals and Alloys (UNS), Society of Automotive Engineers, Warrendale, Pa., 1975. This reference contains the cross reference numbers for AISI, ASTM, FED, MIL SPEC, and SAE specifications. All yield strengths are obtained using the 0.2 percent offset method. Provided by permission from the "Metals Handbook," 8th ed, vol 1, p 414, American Society for Metals, Metals Park, Ohio, 1961. Multiply strength in kpsi be 6.89 to get strength in MPa.)
Yield Tensile Elongation Reduction Brinell
UNS strength, strength, in 2 in, in area, hardness,
number Processing kpsi kpsi % % H_b
------ ------------ --------- --------- ---------- --------- ---------
S20100 Annealed 55 155 55
S20100 1/4 hard 75 125 20
S20100 1/2 hard 110 150 10
S20100 3/4 hard 135 175 5
S20100 Full hard 140 185 4
S20200 Annealed 55 110 55
S20200 1/4 hard 75 125 12
S30100 Annealed 40 110 60 165
S30100 1/4 hard 75 125 25
S30100 1/2 hard 110 150 15
S30100 3/4 hard 135 175 12
S30100 Full hard 140 185 8
S30200 Annealed 37 90 55 65 155
S30200 1/4 hard 75 125 12
S30300 Annealed 35 90 50 55 160
S30400 Annealed 35 85 55 65 150
S31000 Annealed 40 95 45 65 170
S31400 Annealed 50 100 45 60 170
S41400 Annealed 95 120 17 55 235
S41400 Drawn 400 F 150 200 15 55 415
S41400 Drawn 600 F 145 190 15 55 400
S41400 Drawn 800 F 150 200 16 58 415
S41400 Drawn 1000 F 120 145 20 60 325
S41400 Drawn 1200 F 105 120 20 65 260
S41600 Annealed 40 75 30 65 155
S41600 Drawn 400 F 145 190 15 55 390
S41600 Drawn 600 F 140 180 15 55 375
S41600 Drawn 800 F 150 195 17 55 390
S41600 Drawn 1000 F 115 145 20 65 300
S41600 Drawn 1200 F 85 110 23 65 225
S41600 Drawn 1400 F 60 90 30 70 180
S43100 Annealed 95 125 20 60 260
S43100 Drawn 400 F 155 205 15 55 415
S43100 Drawn 600 F 150 195 15 55 400
S43100 Drawn 800 F 155 205 15 60 415
S43100 Drawn 1200 F 95 125 20 60 260
S50100 Annealed 30 70 28 65 160
S50200 Annealed 30 70 30 75 150
------ ------------ --------- --------- ---------- --------- ---------
Shigley, Mechanical Engineering Design, 1980, McGraw Hill